G10 and FR4 glass cloth reinforced epoxy - Natural colors are usually pale yellow to light green. The most versatile all-round laminate grade is a continuous glass woven fabric impregnated epoxy adhesive. Epoxy resin is one of the most versatile and widely used plastics in the electronics industry, primarily because its water absorption is almost zero, making it an excellent insulator.
In addition to its electrical insulating properties, epoxy resins have excellent dimensional stability (typically less than 1% shrinkage) and excellent adhesion properties. G10 / FR4 has extremely high mechanical strength, good dielectric loss performance and good electrical strength properties, whether wet or dry. The main difference between NEMA grades G10 and FR4 is that FR4 is the flame retardant grade of G10. Therefore, in the case where G10 is required, FR4 can be safely replaced, and in the case where FR4 is required, G10 can never be replaced.
Epoxy glass rods are made by boards mill or with rolled and press pre-preg material.
Available in diameter from 4 mm to 150 mm in length 1000 - 1250 - 2000 mm or cut in different sizes.
Made by FR4 - G11 - FR5 - G10 - HGW2372 - EPGC203 can be supply with or without thread.
Technical Parameter:
|
EPOXY GLASS CLOTH LAMINATED SHEET TYPE G-10 |
|||||
|
JY-QC-0920A Date: Jul. 19, 2018 |
|||||
|
No. |
Test Item |
Test condition |
Unit |
Standard Value |
Testing Result |
|
1 |
Density |
‐‐ |
g/cm3 |
≥1.70 |
1.85 |
|
2 |
Moisture Absorption (0.187”) |
ASTM D-570 |
% |
0.15 max |
0.02 |
|
3 |
Breakdown Voltage Condition A |
ASTM D-149 |
kV |
45 min |
50 |
|
4 |
Permittivity (0.187'') Condition A |
ASTM D-150 |
‐‐ |
5.20 |
4.60 |
|
5 |
IZOD Impact Strength (0.187”) Length-Wise |
ASTM D-229 |
ft-lb/in |
7.0 min |
15 |
|
6 |
Flexural Strength (0.187”) Length-Wise |
ASTM D-790 |
ksi (MPa) |
55 (380) min |
80 (552) |
|
7 |
Flexural Modulus (0.187”) Length-Wise |
ASTM D-790 |
psi |
‐‐ |
2,700 |
|
8 |
Tensile Strength (0.125”) Length-Wise |
ASTM D-638 |
psi |
‐‐ |
45,000 |
|
9 |
Compressive Strength |
ASTM D-695 |
psi |
‐‐ |
65,000 |
|
10 |
Hardness Rockwell M |
ASTM D-785 |
‐‐ |
‐‐ |
M110 |
|
11 |
Bonding Strength (0.500”) Condition A |
ASTM D-229 |
Lb (kg) |
2,000 min |
2,300 |
|
12 |
Shear Strength (punch type, 0.125”) |
ASTM D-732 |
ksi (MPa) |
‐‐ |
25 (172) |
|
13 |
Temperature Index |
ASTM D-2304 |
℃ |
‐‐ |
130 |
|
14 |
Coefficient of Linear Thermal Expansion Length-wise |
ASTM D-696 |
X 10-5 in./in./°F |
‐‐ |
0.55 |
|
15 |
Flammability Rating |
UL94 |
Class |
‐‐ |
H-B |
|
16 |
Dissipation Factor @ 1 MHz Condition A |
ASTM D-150 |
‐‐ |
0.025 |
0.018 |
|
17 |
Dielectric Strength (Condition A) |
ASTM D-149 |
V/mil |
‐‐ |
800 |
|
18 |
Arc Resistance (0.125”) |
ASTM D-495 |
Sec |
‐‐ |
130 |
|
19 |
Comparative Tracking Index (0.125”) |
ASTM D-3638 |
V |
‐‐ |
200 |
Advantages:
• High mechanical strength
• Very good electrical isolation
• Low weight
• Easy installation
• High safety against brittle fracture
• High safety against vandalism
Detailed Images:
Packing & Delivery:
The methods employed to pack composite insulators are the result of experience gained from shipping millions of insulators to user warehouses and construction sites in a large number of countries worldwide.The packing method illustrated below have been developed to minimize possible damage during shipment and storage as well as to reduce space and freight cost. The separators are made by wood.
FAQ:
Q:How long is your products warranty ?
A: The warranty period of our products is 18 months.
Q:How about inspection?
A: We have the whole inspection system from raw material to end products include temperature test,strength test and so on.
Q:What do you have for certificate?
A: Our products are passed through ISO9001:2015.
Q:What is payment terms?
A: T.T,Western Union and L/C isacceptable.
Q:What is the service offered by company?
A: We have the professional engineer team which can design and develop the prototype and manufacturing to meet different customer nequirement.
We also have the sales team to offer good service from pre-sale to after-sale.